Rheological properties of nanocellulose suspensions : effects of fibril/particle dimensions and surface characteristics
-
- Moberg, Tobias, 1986 (författare)
- Department of Materials and Manufacturing Technology, Chalmers University of Technology,Chalmers tekniska högskola,Chalmers University of Technology
-
- Sahlin, Karin, 1991 (författare)
- Department of Chemistry and Chemical Engineering, Chalmers University of Technology,Chalmers tekniska högskola,Chalmers University of Technology
-
- Yao, Kun (författare)
- KTH,Glykovetenskap,Wallenberg Wood Science Center,School of Biotechnology, Royal Institute of Technology, Stockholm,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)
-
visa fler...
-
- Geng, Shiyu (författare)
- Luleå tekniska universitet,Materialvetenskap,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH),Luleå tekniska universitet (LTU),Luleå University of Technology (LTU)
-
- Westman, Gunnar, 1964 (författare)
- Department of Chemistry and Chemical Engineering, Chalmers University of Technology,Chalmers tekniska högskola,Chalmers University of Technology
-
- Zhou, Qi (författare)
- KTH,Glykovetenskap,Wallenberg Wood Science Center,School of Biotechnology, Royal Institute of Technology, Stockholm,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH)
-
- Oksman, Kristiina (författare)
- Luleå tekniska universitet,Materialvetenskap,Kungliga Tekniska Högskolan (KTH),Royal Institute of Technology (KTH),Luleå tekniska universitet (LTU),Luleå University of Technology (LTU)
-
- Rigdahl, Mikael, 1950 (författare)
- Department of Materials and Manufacturing Technology, Chalmers University of Technology,Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2017-04-12
- 2017
- Engelska.
-
Ingår i: Cellulose. - : Springer Netherlands. - 0969-0239 .- 1572-882X. ; 24:6, s. 2499-2510
- Relaterad länk:
-
https://link.springe...
-
visa fler...
-
https://research.cha... (primary) (free)
-
https://urn.kb.se/re...
-
https://doi.org/10.1...
-
https://urn.kb.se/re...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- The rheological properties of aqueous suspensions based on three different nanocelluloses were compared. One system was obtained via acid hydrolysis (thus yielding crystalline nanocellulose, CNC) and the other two from mechanical shearing, but from different origins and subjected to different pretreatments. Of the latter two, one was considered to be a rather typical cellulose nanofibril (CNF) suspension whereas the other was a kind of intermediate between CNF and CNC. All three nanocellulose elements differed in dimensions as evident from transmission electron microscopy and atomic force microscopy. With regard to the length of the fibrils/particles, the three nanocelluloses formed three distinct groups with lengths between 200 and slightly more than 800 nm. The three cellulosic elements were also subjected to a TEMPO-mediated oxidation yielding a similar carboxylate content in the three systems. Furthermore, the TEMPO-oxidized elements were grafted with poly(ethylene glycol) (PEG). The amount of grafted PEG was about 35 wt%. The shear viscosity, the storage modulus and the loss modulus of suspensions of the unmodified, the TEMPO-oxidized and the grafted nanocelluloses were determined at room temperature and the solids content of the suspensions was varied between 0.7 and 2.0 wt%. It was concluded that the rheological properties varied significantly between the suspensions depending on the dimensions of the cellulosic elements and their surface characteristics. In this context, the length (or the aspect ratio) of the particles played a very important role.
Ämnesord
- NATURVETENSKAP -- Kemi -- Annan kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Other Chemistry Topics (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Industriell bioteknik -- Biomaterial (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Industrial Biotechnology -- Bio Materials (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Pappers-, massa- och fiberteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Paper, Pulp and Fiber Technology (hsv//eng)
Nyckelord
- Cellulose nanocrystals
- Cellulose nanofibrils
- Rheology
- Surface characteristics
- Trä och bionanokompositer
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Moberg, Tobias, ...
-
Sahlin, Karin, 1 ...
-
Yao, Kun
-
Geng, Shiyu
-
Westman, Gunnar, ...
-
Zhou, Qi
-
visa fler...
-
Oksman, Kristiin ...
-
Rigdahl, Mikael, ...
-
visa färre...
- Om ämnet
-
- NATURVETENSKAP
-
NATURVETENSKAP
-
och Kemi
-
och Annan kemi
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Industriell biot ...
-
och Biomaterial
-
- TEKNIK OCH TEKNOLOGIER
-
TEKNIK OCH TEKNO ...
-
och Materialteknik
-
och Pappers massa oc ...
- Artiklar i publikationen
-
Cellulose
- Av lärosätet
-
Kungliga Tekniska Högskolan
-
Luleå tekniska universitet
-
Chalmers tekniska högskola