Microstructure and ...
Microstructure and mechanical properties of spray formed ultrahigh-carbon steels
-
Zhang, J. G. (författare)
-
Lin, Y. J. (författare)
-
- Hillert, Mats (författare)
- KTH,Materialvetenskap
-
visa fler...
-
- Selleby, Malin (författare)
- KTH,Materialvetenskap
-
Shi, H. S. (författare)
-
Yan, B. (författare)
-
Zhang, H. (författare)
-
Luo, G. M. (författare)
-
Li, X. J. (författare)
-
Wang, J. (författare)
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2004
- 2004
- Engelska.
-
Ingår i: Materials Science & Engineering. - : Elsevier BV. - 0921-5093 .- 1873-4936. ; 383:1, s. 45-49
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The microstructure and mechanical properties of the spray formed 1.25C-3.0Si-1.5Cr ultrahigh-carbon steel (UHCS) were described. The 1.25C-3.0Si-1.5Cr UHCS was processed by spray forming to break up carbide networks. The fine pearlites with average interlamellar spacing of 0.20 mum was observed in the as-sprayed microstructure. The ultimate tensile strength and the pearlite spacing can be related by the Hall-Petch equation. The as-sprayed 1.25C-3.0Si-1.5Cr UHCS consisting of fine lamellar pearlites has been shown to exhibit superplastic behavior at elevated temperature. The dramatic change of microstructure from fine lamellar pearlites to equiaxed grains stabilized by spheroidized particles during superplastic deformation has been observed. The estimation on the basis of thermodynamics shows that the content of chromium of 1.54 wt.% is needed to inhibit graphite formation in the l.25C-3.OSi-1.5Cr UHCS.
Nyckelord
- ultrahigh-carbon steel
- spray forming
- superplasticity
- thermodynamic estimation
- graphitization
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas
- Av författaren/redakt...
-
Zhang, J. G.
-
Lin, Y. J.
-
Hillert, Mats
-
Selleby, Malin
-
Shi, H. S.
-
Yan, B.
-
visa fler...
-
Zhang, H.
-
Luo, G. M.
-
Li, X. J.
-
Wang, J.
-
visa färre...
- Artiklar i publikationen
-
Materials Scienc ...
- Av lärosätet
-
Kungliga Tekniska Högskolan