Effect of Zn addition on dynamic recrystallization behavior of Mg-2Gd alloy during high-temperature deformation

• The effect of Zn/Gd ratio on dynamic recrystallization (DRX) of Mg-2Gd-xZn (x = 0, 1, 2 and 3 wt%) alloys was investigated by shear punch tests in the temperature range of 623-723 K and shear strain rate range of 1.0 x 10(-2)-1.2 x 10(-1) s(-1). It was observed that at low Zn/Gd ratio, excessive co-segregation of Gd and Zn solute atoms retards recrystallization and provides higher strength. At high Zn/Gd ratios, precipitation reduces the co-segregation, so that the alloy with Zn/Gd = 1.5, experienced the fastest DRX and the lowest strength. In addition, segregation resulted in a weaker texture, by elimination of nucleation and growth of the preferred orientations. rights reserved.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

Nyckelord

Magnesium alloys

Grain boundary segregation

Dynamic recrystallization

Shear punch test

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)