Analysis of O-Ring Seal Failure under Static Conditions and Determination of End-of-Lifetime Criterion
-
- Koemmling, Anja (författare)
- Bundesanstalt Mat Forsch & Prufung, D-12200 Berlin, Germany.
-
- Jaunich, Matthias (författare)
- Bundesanstalt Mat Forsch & Prufung, D-12200 Berlin, Germany.
-
- Pourmand, Payam (författare)
- KTH,Fiber- och polymerteknologi
-
visa fler...
-
- Wolff, Dietmar (författare)
- Bundesanstalt Mat Forsch & Prufung, D-12200 Berlin, Germany.
-
- Hedenqvist, Mikael S. (författare)
- KTH,Fiber- och polymerteknologi
-
visa färre...
-
Bundesanstalt Mat Forsch & Prufung, D-12200 Berlin, Germany Fiber- och polymerteknologi (creator_code:org_t)
- 2019-07-29
- 2019
- Engelska.
-
Ingår i: Polymers. - : MDPI. - 2073-4360. ; 11:8
- Relaterad länk:
-
https://www.mdpi.com...
-
visa fler...
-
https://urn.kb.se/re...
-
https://doi.org/10.3...
-
visa färre...
Abstract
Ämnesord
Stäng
- Determining a suitable and reliable end-of-lifetime criterion for O-ring seals is an important issue for long-term seal applications. Therefore, seal failure of ethylene propylene diene rubber (EPDM) and hydrogenated nitrile butadiene rubber (HNBR) O-rings aged in the compressed state at 125 degrees C and at 150 degrees C for up to 1.5 years was analyzed and investigated under static conditions, using both non-lubricated and lubricated seals. Changes of the material properties were analyzed with dynamic-mechanical analysis and permeability experiments. Indenter modulus measurements were used to investigate DLO effects. It became clear that O-rings can remain leak-tight under static conditions even when material properties have already degraded considerably, especially when adhesion effects are encountered. As a feasible and reliable end-of-lifetime criterion for O-ring seals under static conditions should include a safety margin for slight dimensional changes, a modified leakage test involving a small and rapid partial decompression of the seal was introduced that enabled determining a more realistic but still conservative end-of-lifetime criterion for an EPDM seal.
Ämnesord
- NATURVETENSKAP -- Kemi -- Polymerkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Polymer Chemistry (hsv//eng)
Nyckelord
- EPDM
- HNBR
- seal failure
- leak-tightness
- DLO
- oxygen permeability
- DMA