Toughening of a Soft Polar Polythiophene through Copolymerization with Hard Urethane Segments

• Polar polythiophenes with oligoethylene glycol side chains are exceedingly soft materials. A low glass transition temperature and low degree of crystallinity prevents their use as a bulk material. The synthesis of a copolymer comprising 1) soft polythiophene blocks with tetraethylene glycol side chains, and 2) hard urethane segments is reported. The molecular design is contrary to that of other semiconductor-insulator copolymers, which typically combine a soft nonconjugated spacer with hard conjugated segments. Copolymerization of polar polythiophenes and urethane segments results in a ductile material that can be used as a free-standing solid. The copolymer displays a storage modulus of 25 MPa at room temperature, elongation at break of 95%, and a reduced degree of swelling due to hydrogen bonding. Both chemical doping and electrochemical oxidation reveal that the introduction of urethane segments does not unduly reduce the hole charge-carrier mobility and ability to take up charge. Further, stable operation is observed when the copolymer is used as the active layer of organic electrochemical transistors.

Ämnesord

NATURVETENSKAP  -- Kemi -- Polymerkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Polymer Chemistry (hsv//eng)

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Annan kemiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Other Chemical Engineering (hsv//eng)

Nyckelord

chemical and electrochemical doping

organic electrochemical transistors (OECT)

polar conjugated polymers

swelling

urethane

Copolymerization

Crystallinity

Electrochemical oxidation

Glass transition

Glycols

Hall mobility

Hole mobility

Hydrogen bonds

Hydrogen storage

Organic polymers

Semiconductor doping

Thiophene

Degree of swelling

Ductile materials

Elongation at break

Low glass transition temperatures

Oligoethylene glycols

Organic electrochemical transistors

Stable operation

Tetraethylene glycols

Esters

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)