Molecular dynamics of poly(ATRIF) homopolymer and poly(AN-co-ATRIF) copolymer investigated by dielectric relaxation spectroscopy

• Aiming to develop new dielectric polymers containing CN and F groups with strong dipole moments, a novel copolymer of acrylonitrile (AN) and 2,2,2-trifluoroethyl acrylate (ATRIF) was synthesized in acetonitrile by free radical process as well as the respective homopolymer (poly(ATRIF)). The copolymer's composition and microstructure were analyzed by FTIR, (1)H and (13)C NMR spectroscopy and SEC. The molar incorporation of AN determined in the copolymer by NMR was 58 mol%. Thermogravimetric analysis of poly(AN-co-ATRIF) copolymer showed good thermal stability comparatively to the fluorinated homopolymer. Both copolymer, poly(AN-co-ATRIF), and homopolymer, poly(ATRIF), were dielectrically characterized over a frequency range from 10(-1) to 10(6) Hz, and in a temperature range from 223 to 393 K. The dominating relaxation process detected in both materials is the alpha-relaxation, associated with the dynamic glass transition. A VFTH temperature dependence of the relaxation times (tau) was found for both materials, as characteristic of cooperative processes, from which the respective glass transition temperatures (T(g)(tau = 100 s)) were estimated, which differ similar to 40 K, the one of the copolymer being higher (307 K) in accordance to the calorimetric analysis. This effect was attributed to a higher stiffness of the backbone in the copolymer originated by the inclusion of the acrylonitrile groups. Both relaxation functions have the same breath of relaxation times allowing constructing a single master curve, indicating similar non-exponential character. A less fragile behavior was found for the copolymer. This was rationalized in a more straightforward way by the free volume approach instead from a correlation between fragility and intermolecular coupling. It was found that in the copolymer the free volume increases at a lower rate with the temperature increase. It was inferred from the VFTH temperature dependence of the dc conductivity and low values of the decoupling index that ion motion is significantly influenced by the dynamics of the alpha-process.

Ämnesord

NATURVETENSKAP  -- Kemi -- Polymerkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Polymer Chemistry (hsv//eng)

Nyckelord

Dielectric polymers

Poly(ATRIF)

Dielectric spectroscopy

Secondary relaxations

NMR characterization

Polymer chemistry

Polymerkemi

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)