Time- and Cycle-Dependent Crack Propagation in Haynes 282

• Haynes 282 is a promising superalloy candidate for several high-temperature applications in both aero and land-based gas turbine engines. To study the crack growth behaviour under time-dependent conditions relevant to such applications, a test program was carried out at room temperature up to 700 °C with conditions ranging from pure cyclic to sustained tensile loading. At 650 °C and high stress intensity factors the crack growth was fully time-dependent for dwell-times of 90 s and longer. At lower stress intensities, the behaviour was mainly controlled by the cyclic loading, even under dwell conditions. The behaviour under dwell-fatigue conditions was well described by a liner superposition model.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

Nyckelord

Nickel based superalloys

fatigue

fracture

mechanical characterisation

electron microscopy

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)