MXene//MnO2 Asymmetric Supercapacitors with High Voltages and High Energy Densities

• Aqueous asymmetric supercapacitors (AASCs) can have high voltages and high energy densities. However, the rational design of AASCs with proper negative and positive electrodes remains a challenge. Herein, we report on an AASC using Mo1.33CTz MXene films as the negative electrode, and tetramethylammonium cation intercalated birnessite (TMA(+)-MnO2) films as the positive electrode in a 21 mol kg(-1) lithium bis(trifluoromethanesulphonyl)imide (LiTFSI) electrolyte. Benefiting from a high, stable voltage of 2.5 V, an energy density of 86.5 Wh L-1 at 2 mV s(-1) and a power density of 10.3 kW L-1 at 1 Vs(-1) were achieved. The cells also exhibit excellent cycling stability (>98% after 1,0000 cycles at 100 mV s(-1)) and a 51.1 % voltage retention after 10 h. This good performance is attributed to the high stable potential window and high volumetric capacitances of both Mo1.33CTz and TMA(+)-MnO2 electrodes in highly concentrated electrolytes. This work provides a roadmap for developing high performance AASCs with high voltages and high energy/power densities, with relatively slow self-discharge rates.

Ämnesord

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)

Nyckelord

birnessite MnO2; high energy density; high voltage; MXene; supercapacitors

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)