A study of thick 3C-SiC epitaxial layers grown on 6H-SiC substrates by sublimation epitaxy in vacuum

• 3C-SiC epitaxial layers with a thickness of up to 100 μm were grown on 6H-SiC hexagonal substrates by sublimation epitaxy in vacuum. The n-type epitaxial layers with the area in the range 0.3-0.5 cm2 and uncompensated donor concentration N d - N a ∼ (10 17-1018) cm-3 were produced at maximum growth rates of up to 200 μm/h. An X-ray analysis demonstrated that the epitaxial layers are composed of the 3C-SiC polytype, without inclusions of other polytypes. The photoluminescence (PL) spectrum of the layers was found to be dominated by the donor-acceptor (Al-N) recombination band peaked at hv ≈ 2.12 eV. The PL spectrum measured at 6 K was analyzed in detail. It is concluded that the epitaxial layers obtained can serve as substrates for 3C-SiC-based electronic devices. © Nauka/Interperiodica 2007.