Influence of synthesis temperature on morphology of SBA-16 mesoporous materials with a three-dimensional pore system

• Spherical particles of mesoporous silica SBA-16 with cubic Im3m structure were synthesized at low pH using Pluronic F127 as template and TEOS as silica source. The diameter of the spherical particles can be controlled in the range of 0.5–8 μm by varying synthesis temperature from 1 °C up to 40 °C. A sharp transition from large particle sizes at approximately 20 °C to smaller ones is observed when the temperature is increased. It is suggested that this morphology transition is due to a change in hydrolysis and condensation rate of the silica source and as a result the assembly of F127 micelles will differ. The SBA-16 samples were characterized using powder X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and nitrogen adsorption techniques.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Annan teknik -- Övrig annan teknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Other Engineering and Technologies -- Other Engineering and Technologies not elsewhere specified (hsv//eng)

Nyckelord

SBA-16; Spherical particles; Synthesis temperature; Morphology; F127

Material physics with surface physics

Materialfysik med ytfysik

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)