Defects in low-energy electron-irradiated n-type 4H-SiC

• The bistable M-center, previously observed in high-energy proton-implanted 4H-SiC, was detected in low-energy electron-irradiated 4H-SiC using deep-level transient spectroscopy (DLTS). Irradiation increased the DLTS signals of the intrinsic defects Z(1/2) and EH6/7 and introduced the frequently observed defects EH1 and EH3. After the M-center is annealed out at about 650K without bias and at about 575K with bias applied to the sample during the annealing process, a new bistable defect in the low temperature range of the DLTS spectrum, the EB-center, evolves. Since low-energy irradiation affects mainly the carbon atoms in SiC, the M-center and the newly discovered EB-center are most probably carbon-related intrinsic defects.