Study of adhesive bondlines in modified wood with fluorescence microscopy and X-ray micro-computed tomography
-
- Bastani, Alireza (författare)
- Georg-August-University Göttingen, Germany
-
- Adamopoulos, Stergios (författare)
- Linnéuniversitetet,Institutionen för skog och träteknik (SOT),GoFP
-
- Koddenberg, Tim (författare)
- Georg-August-University Göttingen, Germany
-
visa fler...
-
- Militz, Holger (författare)
- Georg-August-University Göttingen, Germany
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2016
- 2016
- Engelska.
-
Ingår i: International Journal of Adhesion and Adhesives. - : Elsevier BV. - 0143-7496 .- 1879-0127. ; 68, s. 351-358
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The quantitative penetration of three coldset wood adhesives [one-component polyurethane (PU), emulsion polymer isocyanate (EPI), poly (vinyl acetate) (PVAc)] under hydraulic pressure into different types of modified wood was studied using fluorescence microscopy and the results were compared to these of a previous study without pressure on adjacent wood samples. The effective penetration (EP) of PU was negatively affected by furfurlylation and NMM modification when pressure was applied. For PVAc, 30% NMM treatment and heat treatment of Scots pine and beech at 210 °C had a negative effect on its EP, but against this the EP of this adhesive increased after heat treatment of beech at 195 °C. In the case of furfurylation, the depth of penetration of all adhesives was less into wood treated with higher concentration of furfuryl alcohol. PU showed a much deeper penetration into NMM-modified and heat-treated wood than the other adhesives with the exception of heat-treated beech at 195 °C. Application of pressure led to rather different results as compared to the EP data when no pressure was applied. The three-dimensional (3D) visualisation of the penetration of PU adhesive into heat-treated Scots pine was also examined by X-ray micro-computed tomography (XµCT). The 3D flow pattern of PU adhesive into heat-treated Scots pine was clearly depicted by XµCT.
Ämnesord
- LANTBRUKSVETENSKAPER -- Lantbruksvetenskap, skogsbruk och fiske -- Trävetenskap (hsv//swe)
- AGRICULTURAL SCIENCES -- Agriculture, Forestry and Fisheries -- Wood Science (hsv//eng)
Nyckelord
- Modified wood
- Adhesive penetration
- Bondline
- Fluorescence microscopy
- X-ray tomography
- Forestry and Wood Technology
- Skog och träteknik
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas