Elastic strain at semi-isostatic compression of Scots pine (Pinus sylvestris)

• Quarter-sawn and plain-sawn specimens of Scots pine were semi-isostatically compressed at 5, 15, 50, and 140MPa in a Quintus press. Elastic strain was measured using a telescope device that was pushed together when wood was compressed and remained in this position at release of pressure. Delayed elastic and plastic strains were assessed through repeated callipering during 5 years after densification. At 140MPa, wood reached an almost compact structure (ρ ≈ 1450kg/m3) but as a result of elastic springback the density decreased to just below 1000kg/m3. At 140MPa, the elastic and delayed elastic strains were 14.6% and 1.8%, respectively, in quarter-sawn specimens, and were 13.1% and 0.8%, respectively, in plain-sawn specimens. The higher elastic strains in quarter-sawn specimens can be attributed to elastic springback in the tangentially deformed latewood bands

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Annan maskinteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Other Mechanical Engineering (hsv//eng)

LANTBRUKSVETENSKAPER  -- Lantbruksvetenskap, skogsbruk och fiske (hsv//swe)

AGRICULTURAL SCIENCES  -- Agriculture, Forestry and Fisheries (hsv//eng)

Nyckelord

Träteknik

Wood Technology

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)