Aluminophosphate monoliths with high CO2-over-N2 selectivity and CO2 capture capacity

• Monoliths of microporous aluminophosphates (AlPO4-17 and AlPO4-53) were structured by binder-free pulsed current processing. Such monoliths could be important for carbon capture from flue gas. The AlPO4-17 and AlPO4-53 monoliths exhibited a tensile strength of 1.0 MPa and a CO2 adsorption capacity of 2.5 mmol g-1 and 1.6 mmol g-1, respectively at 101 kPa and 0°C. Analyses of single component CO2 and N2 adsorption data indicated that the AlPO4-53 monoliths had an extraordinarily high CO2-over-N2 selectivity from a binary gas mixture of 15 mol% CO2 and 85 mol% N2. The estimated CO2 capture capacity of AlPO4-17 and AlPO4-53 monoliths in a typical pressure swing adsorption (PSA) process at 20°C was higher than that of the commonly used zeolite 13X granules. Under cyclic sorption conditions, AlPO4-17 and AlPO4-53 monoliths were regenerated by lowering the pressure of CO2. Regeneration was done without application of heat, which would regenerate them to their full capacity for CO2 adsorption.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

Nyckelord

Materialteknik

Engineering Materials

Materials Chemistry

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)