Spark plasma synthesis and sintering of superconducting MgB 2-based materials

Prikhna, Tatiana (författare)
Institute for Superhard Materials, National Academy of Sciences of Ukraine, Kiev, 04074, 2 Avtozavodskaya Street, Ukraine
Noudem, Jacques (författare)
CNRS/CRISMAT, Juin14050 Caen, 6, Bd du Maréchal, France
Gawalek, Wolfgang (författare)
Institut für Photonische Technologien, Jena, D07745, Albert-Einstein-Strasse 9, Germany
visa fler...
Mamalis, Athanasios (författare)
National Technical University of Athens, Athens 15780, Iroon Polytechiou, 9, Greece
Soldatov, Alexander (författare)
Luleå tekniska universitet,Materialvetenskap
Savchuk, Yaroslav (författare)
Institute for Superhard Materials, National Academy of Sciences of Ukraine, Kiev, 04074, 2 Avtozavodskaya Street, Ukraine
Moshchil, Viktor (författare)
Institute for Superhard Materials, National Academy of Sciences of Ukraine, Kiev, 04074, 2 Avtozavodskaya Street, Ukraine
Eisterer, Michael (författare)
Atomic Institute of Austrian Universities, 1020 Vienna, Austria
Weber, Harald W. (författare)
Atomic Institute of Austrian Universities, 1020 Vienna, Austria
Dub, Sergey (författare)
Institute for Superhard Materials, National Academy of Sciences of Ukraine, Kiev, 04074, 2 Avtozavodskaya Street, Ukraine
Habisreuther, Tobias (författare)
Institut für Photonische Technologien, Jena, D07745, Albert-Einstein-Strasse 9, Germany
Dellith, Jan (författare)
Institut für Photonische Technologien, Jena, D07745, Albert-Einstein-Strasse 9, Germany
You, Shujie (författare)
Luleå tekniska universitet,Materialvetenskap
Schmidt, Christa (författare)
Institut für Photonische Technologien, Jena, D07745, Albert-Einstein-Strasse 9, Germany
Karau, Friedrich (författare)
H.C. Starck GmbH, Goslar 38642, Germany
Dittrich, Ulrich (författare)
H.C. Starck GmbH, Goslar 38642, Germany
Vajda, István (författare)
Budapest University of Technology and Economics, 1111 Budapest, Egry Jozsef u. 18, Hungary
Sergienko, Nina (författare)
Institute for Superhard Materials, National Academy of Sciences of Ukraine, Kiev, 04074, 2 Avtozavodskaya Street, Ukraine
Sokolovsky, Vladimir (författare)
Ben-Gurion University of Negev, Beer-Sheva 84105, P.O.B. 653, Israel
Litzkendorf, Doris (författare)
Institut für Photonische Technologien, Jena, D07745, Albert-Einstein-Strasse 9, Germany
Chaud, Xavier (författare)
CNRS/CRETA, 38042 Grenoble CEDEX 9, 25, Avenue des Martyrs, France
Sverdun, Vladimir (författare)
Institute for Superhard Materials, National Academy of Sciences of Ukraine, Kiev, 04074, 2 Avtozavodskaya Street, Ukraine
Kuznietsov, Roman (författare)
Institute for Superhard Materials, National Academy of Sciences of Ukraine, Kiev, 04074, 2 Avtozavodskaya Street, Ukraine
visa färre...
 (creator_code:org_t)
Trans Tech Publications Inc. 2012
2012
Engelska.
Ingår i: Applied Electromagnetic Engineering for Magnetic, Superconducting and Nano Materials. - : Trans Tech Publications Inc.. - 9783037854204 ; , s. 42437-
Relaterad länk:
https://urn.kb.se/re...
visa fler...
https://doi.org/10.4...
visa färre...
  • Konferensbidrag (refereegranskat)
Abstract Ämnesord
Stäng  
  • Superconducting (SC) and mechanical properties of spark plasma (or SPS) produced MgB 2 -based materials allow their efficient applications in fault current limiters, superconducting electromotors, pumps, generators, magnetic bearings, etc. The synthesized from Mg and B at 50 MPa, 1050 °C for 30 min material has a density of 2.52 g/cm 3, critical current density, j c = 7.1·10 5 A/cm 2 at 10 K , 5.4·10 5 A/cm 2 at 20 K, and 9·10 4 A/cm 2 at 35 K in zero magnetic field; at 20 K its field of irreversibility B irr(20)=7 T and upper critical field B c2(20)=11 T; microhardness H V=10.5 GPa and fracture toughness K 1C =1.7 MPa·m 1/2 at 4.9 N-load. SPS-manufactured in- situ MgB 2- based materials usually have somewhat higher j c than sintered ex-situ. The pressure variations from 16 to 96 MPa during the SPS-process did not affect material SC characteristics significantly; the j c at 10-20 K was slightly higher and the material density was higher by 11%, when pressures of 50-96 MPa were used. The structure of SPS-produced MgB 2 material contains Mg-B-O inclusions and inclusions of higher borides (of compositions near MgB 4, MgB 7, MgB 12, MgB 17, MgB 20), which can be pinning centers. The presence of higher borides in the MgB 2 structure can be revealed by the SEM and Raman spectroscopy.

Ämnesord

NATURVETENSKAP  -- Fysik -- Annan fysik (hsv//swe)
NATURAL SCIENCES  -- Physical Sciences -- Other Physics Topics (hsv//eng)

Nyckelord

Experimentell fysik
Experimental Physics

Publikations- och innehållstyp

ref (ämneskategori)
kon (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy