Microstructures of high strength steel welding consumables from directed thermal cycles by shaped laser pulses

• Filler wire metallurgy was modified through temporally shaped laser pulses, controlling cooling cycles in a recently developed method. Trends were identified through efficient mapping while maintaining representative thermal cycles of welding processes. A primary pulse melted preplaced filler wires while a secondary, linearly ramped-down pulse elevated the nugget to re-austenization temperatures. Ramped-down pulses resulted in linear cooling rates comparable with and exceeding furnace-based methods, between 50 and 300∘C/s. The linear decay of laser output power guided the temperature through a regime to obtain desired microstructures. For three very high-strength steel filler wire chemistries, quenching resulted in smaller plates with cross-hatched microstructures, accompanied by grain boundary ferrite. Finer bainite microstructures started forming for fast linear temperature decay, about 250∘C/s. Slower decay or a weaker third cycle formed coarser microstructures with coalescent sheaves and less cross-hatching.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Bearbetnings-, yt- och fogningsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Manufacturing, Surface and Joining Technology (hsv//eng)

Nyckelord

filler wire

consumable

welding

thermal cycle

microstructure

cooling rate

Produktionsutveckling

Manufacturing Systems Engineering

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)