Bacterial cellulose assisted synthesis of hierarchical pompon-like SAPO-34 for CO2 adsorption

• In the present work, a biosynthesis route for the preparation of hierarchical pompon-like SAPO-34 was developed. Commercially available bacterial cellulose aerogel was used as template. SiO2 loaded bacterial cellulose aerogel was used as silica source and a simple hydrothermal treatment was used for crystallization. XRD, FT-IR, SEM, TEM, N2 adsorption-desorption and TG techniques were employed to characterize the obtained samples. The hierarchical pompon-like SAPO-34 showed a spherical morphology that was comprised of nanosheets with a thickness less than 30 nm. The specific surface area of the hierarchical pompon-like SAPO-34 was 498 m2/g that was higher than the trigonal SAPO-34 crystals of 465 m2/g. The ultrasonic treatment experiment indicated a high stability of the pompon-like structure. In addition, the hierarchical pompon-like SAPO-34 exhibited a CO2 adsorption capacity of 2.26 mmol/g at 100 kPa and 298K and the corresponding CO2/CH4 ideal separation factor was 5.7, which was higher than that of trigonal SAPO-34 crystals. The saturated adsorption capacity and b-value were estimated using single site Langmuir, Toth and Sips adsorption isotherm models and the observed results were constant. Compared with trigonal SAPO-34, hierarchical pompon-like SAPO-34 displayed a higher saturated adsorption capacity, but a lower b-value.

Ämnesord

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

Nyckelord

Adsorption

Aerogels

Biochemistry

Carbon dioxide

Cellulose

Crystal structure

Morphology

Silica gel

B value

Bacterial cellulose

Biosynthesis route

Cellulose aerogels

CO2 adsorption

Hierarchical pompon-like SAPO-34

SAPO-34

Saturated adsorption capacity

Silica sources

Simple+

Biosynthesis

Chemical Technology

Kemisk teknologi

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)