Bone response to physical-vapour-deposited titanium dioxide coatings on titanium implants
-
- Ballo, Ahmed, 1978 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap,Institute of Clinical Sciences, Department of Biomaterials
-
- Björn, Dorota (författare)
- Sandvik, Sweden
-
- Åstrand, Maria (författare)
- Sandvik, Sweden
-
visa fler...
-
- Palmquist, Anders, 1977 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap,Institute of Clinical Sciences, Department of Biomaterials
-
- Lausmaa, Jukka (författare)
- RISE,SP – Sveriges Tekniska Forskningsinstitut / Funktionella material (KMf)
-
- Thomsen, Peter, 1953 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap,Institute of Clinical Sciences, Department of Biomaterials
-
visa färre...
-
(creator_code:org_t)
- 2012-06-15
- 2013
- Engelska.
-
Ingår i: Clinical Oral Implants Research. - : Wiley. - 0905-7161 .- 1600-0501. ; 24:9, s. 1009-1017
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
https://gup.ub.gu.se...
-
visa färre...
Abstract
Ämnesord
Stäng
- Objectives: The aim of this study was to investigate the correlation between coating thickness and the crystal structure of physical-vapour-deposited (PVD) titanium dioxide coatings, and to evaluate their in vivo biocompatibility. Materials and methods: The PVD TiO 2 coatings of different thickness were deposited on machined titanium grade 2 screw-shaped implants. Non-coated titanium implants were used as controls. Coating properties such as thickness, crystal structure, coating morphology and roughness were characterized. Forty-eight implants were placed randomly into both tibias of 16 rats. The animals were euthanized 7 and 28 days postsurgery and block biopsies were prepared for histology, histomorphometry and SEM analysis. Results: The thicknesses of the PVDTiO 2 coatings were 120 and 1430 nm respectively. Histologically, new bone formed on all implant surfaces. The mean percentage of newly formed bone in contact with the implant (BIC) was significantly higher at early healing time (7 days) for the 120 nm thick PVD coating (39 ± 14%) than for both the 1430 nm thick PVD coating (22 ± 10%) (P = 0.043) and the machined surface (22 ± 9%) (P = 0.028). This difference was no longer evident after 28 days (P = 0.867). Conclusion: Bone formation and bone-to-implant contact are achieved to the same degree for TiO 2 surface modifications prepared by a PVD process as clinically used, machined titanium. Furthermore, a relatively thinner PVD coating promotes a higher degree of bone apposition shortly after implantation, thereby providing rationales for exploring the potential clinical use of these modifications.
Ämnesord
- MEDICIN OCH HÄLSOVETENSKAP -- Medicinsk bioteknologi -- Biomaterialvetenskap (hsv//swe)
- MEDICAL AND HEALTH SCIENCES -- Medical Biotechnology -- Biomaterials Science (hsv//eng)
Nyckelord
- implant; in vivo; osseointegration; surface coating; surface modification; titanium dioxide