Interaction between ash forming elements in woody biomass and two high alumina refractories part 2 : transformation of crystalline compounds

• Two high alumina refractories, one brick and one pre fired castable was exposed to pure K2CO3, K2CO3 + CaCO3, and K2CO3 + CaCO3 + SiO2 at 1050°C and a CO2 atmosphere. A stratified investigation of crystalline phases was made with polycrystalline x-ray diffraction, and thermodynamic equilibrium calculations were performed to explore possible formation paths. A monoclinic polymorph of KAlSiO4 was formed to a large extent in both materials exposed to pure K2CO3. Throughout the affected part of the castable and a small layer close to the surface of the brick, a solid solution between KAlO2 and KAlSiO4 formed, K1-xAl1-xSixO2, x = 0.19. The affected area of the castable had 30-50 %wt new phases and made a sharp transition to unaffected material. The concentration of new phases in the brick was decreasing at an even rate from about 40 to 15%wt throughout the whole material thickness of 14 mm. Exposure to K2CO3 and CaCO3 showed the same phases and behavior, but no Ca-bearing phases could be detected. The mixture containing K2CO3, CaCO3 and SiO2 did not penetrate far into the material but formed the same phases in the affected areas. Wollastonite (CaSiO3) formed in the slag on top of these materials. The major mechanism for formation of new phases is suggested to be the formation of an initial melt composed of K2O and SiO2. This liquid is then dissolving refractory components and forms a liquid in equilibrium with KAlSiO4 and K1-xAl1-xSixO2.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Keramteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Ceramics (hsv//eng)

Nyckelord

Refractory corrosion

slag

biomass

gasification

phase transformation

Materials Science

materialvetenskap

Publikations- och innehållstyp

vet (ämneskategori)

ovr (ämneskategori)