Tailoring magnetism at the nanometer scale in SmCo5 amorphous films
-
- Moubah, Reda (författare)
- Uppsala universitet,Materialfysik
-
- Magnus, Fridrik (författare)
- Uppsala universitet,Materialfysik
-
- Östman, Erik (författare)
- Uppsala universitet,Institutionen för fysik och astronomi
-
visa fler...
-
- Muhammad, Yousuf (författare)
- Uppsala universitet,Institutionen för fysik och astronomi
-
- Arnalds, Unnar B. (författare)
- Uppsala universitet,Materialfysik
-
- Ahlberg, Martina (författare)
- Uppsala universitet,Materialfysik
-
- Hjörvarsson, Björgvin (författare)
- Uppsala universitet,Materialfysik
-
- Andersson, Gabriella (författare)
- Uppsala universitet,Materialfysik
-
visa färre...
-
(creator_code:org_t)
- 2013-09-18
- 2013
- Engelska.
-
Ingår i: Journal of Physics. - : IOP Publishing. - 0953-8984 .- 1361-648X. ; 25:41, s. 416004-
- Relaterad länk:
-
https://urn.kb.se/re...
-
visa fler...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The thickness dependence of magnetic properties has been studied in SmCo5 amorphous films with imprinted in-plane anisotropy for thicknesses ranging down to the nanometer scale (2.5-100 nm). The field induced in-plane magnetic anisotropy decreases considerably when the film thickness is below 20 nm. Analysis of the magnetic anisotropy energy shows that the decrease of the induced in-plane anisotropy is accompanied by the development of an out-of-plane interface anisotropy. Two different regimes for the coercivity (H-c) change are found: below 3.75 nm, the H-c decreases continuously with decrease of the film thickness, whereas at above 3.75 nm, the H-c decreases with increase of the film thickness. This change in Hc can be understood by considering the decrease of the short range chemical order for the thinnest films (<3.75 nm) and the relative decrease of the interface contribution with increasing film thickness. The changes in anisotropy have a profound influence on the domain structure, in which the angle of the zigzag domain boundaries decreases with the inverse thickness of the layers.