Emulsion-templated bicontinuous carbon network electrodes for use in 3D microstructured batteries

• High surface area carbon foams were prepared and characterized for use in 3D structured batteries. Twopotential applications exist for these foams: firstly as an anode and secondly as a current collector supportfor electrode materials. The preparation of the carbon foams by pyrolysis of a high internal phase emulsionpolymer (polyHIPE) resulted in structures with cage sizes of 25 mm and a surface area enhancement pergeometric area of approximately 90 times, close to the optimal configuration for a 3D microstructuredbattery support. The structure was probed using XPS, SEM, BET, XRD and Raman techniques; revealingthat the foams were composed of a disordered carbon with a pore size in the <100 nm range resultingin a BET measured surface area of 433 m2 g-1. A reversible capacity exceeding 3.5 mA h cm2 at acurrent density of 0.37 mA cm-2 was achieved. SEM images of the foams after 50 cycles showed thatthe structure suffered no degradation. Furthermore, the foams were tested as a current collector bydepositing a layer of polyaniline cathode over their surface. High footprint area capacities of500 mA h cm-2 were seen in the voltage range 3.8 to 2.5 V vs. Li and a reasonable rate performancewas observed.

Ämnesord

NATURVETENSKAP  -- Kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

Nyckelord

Carbon foam

High internal phase emulsion polymer

microbattery

3D microbattery

Lithium ion

Materialvetenskap

Materials Science

Chemistry

Kemi

Materialvetenskap

Materials Science

Fysikalisk kemi

Physical Chemistry

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)