Crack initiation and early propagation in case hardened sintered PM steels under cyclic load

• In the present study, crack propagation through the case hardened region of two different PM steels manufactured with different powder size distributions and sintered at different temperatures has been investigated. EBSD was used to study the microstructure before and after case hardening, revealing the relationship between powder particle grains after sintering and prior austenite grains after case hardening. A novel approach was used to achieve short cracks (10–20 µm) with high repeatability. The cracks were then analysed using EBSD and SEM, revealing detailed and novel information about the crack propagation route in the materials. Both tested materials show the same crack propagation behaviour. If a prior grain/prior austenite boundary is present within an angle from the crack initiation site, the cracks will follow the boundary and thus propagate intergranular, suggesting that the preferred route of crack propagation in case hardened sintered steel is along these boundaries.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

PM steel

fatigue

crack initiation

crack propagation

EBSD

Teknisk fysik med inriktning mot tribomaterial

Engineering Science with specialization in Tribo Materials

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)