TbMgNi4-xCox-(H,D)2 System. II : Correlation between Structural and Magnetic Properties

• The magnetic properties of TbMgNi4-xCox intermetallic compounds and selected hydrides and deuterides of this system have been studied by various techniques, including magnetic measurements, in situ X-ray and neutron powder diffraction. The intermetallic compounds crystallize in a SnMgCu4-type structure and magnetically order below a Curie temperature (T-C), which increases exponentially with the Co content. This can be due to the ordering of the Co sublattice. On the other hand, the insertion of D or H in TbMgNiCo3 strongly decreases T-C. The X-ray diffraction measurements versus temperature reveal cell volume minima at T-C for the compounds with x = 1-3 without any hints of the structure change. The analysis of the neutron diffraction patterns for the intermetallics with x = 2 and 3 indicates a slightly canted ferrimagnetic structure below T-C. The Tb moments refined at 16 K are 4.1(2) (mu B)/Tb for x = 2, and 6.2(1) mu B/Tb for x = 3, which are smaller than the free ion value (9.5 mu B/Tb). This reduction can be due to the influence of temperature but also reveals the crystal field effect. As Ni and Co occupy statistically the same Wyckoff site, an average Ni/Co moment was refined, leading to 1.7(2) (mu B)/atom for x = 2 and 1.8(1) mu B/atom for x = 3 at 16 K. This moment is slightly canted compared to the Tb moment.

Subject headings

NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)

Publication and Content Type

ref (subject category)

art (subject category)