High light-to-energy conversion efficiencies for solar cells based on nanostructured ZnO electrodes
-
- Rensmo, Håkan (författare)
- Uppsala universitet,Fysikalisk-kemiska institutionen
-
- Keis, Karin (författare)
- Uppsala universitet,Fysikalisk-kemiska institutionen
-
- Lindström, Henrik (författare)
- Uppsala universitet,Fysikalisk-kemiska institutionen
-
visa fler...
-
- Södergren, Sven (författare)
- Uppsala universitet,Fysiska institutionen
-
- Solbrand, Anita (författare)
- Uppsala universitet,Fysikalisk-kemiska institutionen
-
- Hagfeldt, Anders (författare)
- Uppsala universitet,Fysikalisk-kemiska institutionen
-
- Lindquist, Sten-Eric (författare)
- Uppsala universitet,Fysikalisk-kemiska institutionen
-
Wang, Lingna (författare)
-
Muhammed, M (författare)
-
visa färre...
-
(creator_code:org_t)
- AMER CHEMICAL SOC, 1997
- 1997
- Engelska.
-
Ingår i: Journal of Physical Chemistry B. - : AMER CHEMICAL SOC. - 1520-6106 .- 1520-5207. ; 101:14, s. 2598-2601
- Relaterad länk:
-
https://urn.kb.se/re...
Abstract
Ämnesord
Stäng
- Photoelectrochemical properties of nanostructured ZnO thin film electrodes have been investigated in the UV and visible regions. For films consisting of 15 nm large undoped crystallites a maximum monochromatic current conversion efficiency of 58% was obtained in the visible using a ruthenium-based dye as a sensitizer. The overall solar energy conversion efficiency for this film was 2%. In comparison, sensitized films consisting of 150 nm large Al-doped crystallites yield a monochromatic current conversion efficiency of 31% and an overall solar energy conversion efficiency of 0.5%. The study also shows that nanostructured ZnO may give high efficiencies in the UV region, approaching unity for the Al-doped films.
Nyckelord
- Colloidal TIO2 Films
- Photoelectrochemical Cells
- Nanocrystalline
- Sensitization
- NATURAL SCIENCES
- NATURVETENSKAP
Publikations- och innehållstyp
- vet (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas