Tribological Characterisation of an Organic Coating by the use of ToF-SIMS
-
- Bexell, Ulf (författare)
- Högskolan Dalarna,Materialvetenskap
-
- Carlsson, Per (författare)
- Högskolan Dalarna,Materialvetenskap
-
- Olsson, Mikael (författare)
- Högskolan Dalarna,Materialvetenskap
-
(creator_code:org_t)
- 2003
- 2003
- Engelska.
-
Ingår i: Applied Surface Science. - 0169-4332 .- 1873-5584. ; 203-204, s. 596-599
- Relaterad länk:
-
https://urn.kb.se/re...
Abstract
Ämnesord
Stäng
- ToF-SIMS has been used to analyse tribological induced chemical changes of organic coatings deposited on steel strip hot-dip coated with a 55.0% Al–43.4% Zn–1.6% Si alloy (Aluzink). The organic coating was a styrene–acrylic co-polymer containing different forming additives. The forming properties of the organic coatings were evaluated with modified scratch testing. The friction curves show that organic coated hot-dip coated steel displays significantly better tribological properties, i.e. lower coefficient of friction and lower wear, as compared to hot-dip coated steel. Furthermore, the organic coatings showing the highest material transfer tendency also show the highest wear. ToF-SIMS spectra show that a transfer film consisting of species from the organic coating is formed on the ball counter surface. Finally, a combination of SEM and ToF-SIMS analysis shows that mechanical failure of the coating dominates, i.e. no tribochemical changes of the coatings could be detected in the wear track.
Nyckelord
- Thin organic coatings; Hot-dip coated steel; Friction; Wear; ToF-SIMS