Surface Chemistry, Structure, and Electronic Properties from Microns to the Atomic Scale of Axially Doped Semiconductor Nanowires.

Hjort, Martin (författare)
Lund University,Lunds universitet,Synkrotronljusfysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Synchrotron Radiation Research,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Wallentin, Jesper (författare)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Timm, Rainer (författare)
Lund University,Lunds universitet,Synkrotronljusfysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Synchrotron Radiation Research,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
visa fler...
Zakharov, Alexei (författare)
Lund University,Lunds universitet,MAX IV-laboratoriet,MAX IV Laboratory
Håkanson, Ulf (författare)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Andersen, Jesper N (författare)
Lund University,Lunds universitet,Synkrotronljusfysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Synchrotron Radiation Research,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Lundgren, Edvin (författare)
Lund University,Lunds universitet,Synkrotronljusfysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Synchrotron Radiation Research,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Samuelson, Lars (författare)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Borgström, Magnus (författare)
Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
Mikkelsen, Anders (författare)
Lund University,Lunds universitet,Synkrotronljusfysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Synchrotron Radiation Research,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
visa färre...
 (creator_code:org_t)
2012-10-24
2012
Engelska.
Ingår i: ACS Nano. - : American Chemical Society (ACS). - 1936-086X .- 1936-0851.
Relaterad länk:
http://dx.doi.org/10...
visa fler...
https://lup.lub.lu.s...
https://doi.org/10.1...
visa färre...
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • Using both synchrotron-based photoemission electron microscopy/spectroscopy and scanning tunneling microscopy/spectroscopy, we obtain a complete picture of the surface composition, morphology, and electronic structure of InP nanowires. Characterization is done at all relevant length scales from micrometer to nanometer. We investigate nanowire surfaces with native oxide and molecular adsorbates resulting from exposure to ambient air. Atomic hydrogen exposure at elevated temperatures which leads to the removal of surface oxides while leaving the crystalline part of the wire intact was also studied. We show how surface chemical composition will seriously influence nanowire electronic properties. However, opposite to, for example, Ge nanowires, water or sulfur molecules adsorbed on the exterior oxidized surfaces are of less relevance. Instead, it is the final few atomic layers of the oxide which plays the most significant role by strongly negatively doping the surface. The InP nanowires in air are rather insensitive to their chemical surroundings in contrast to what is often assumed for nanowires. Our measurements allow us to draw a complete energy diagram depicting both band gap and differences in electron affinity across an axial nanowire p-n junction. Our findings thus give a robust set of quantitative values relating surface chemical composition to specific electronic properties highly relevant for simulating the performance of nanoscale devices.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Nanoteknik -- Nanoteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Nano-technology -- Nano-technology (hsv//eng)

Publikations- och innehållstyp

art (ämneskategori)
ref (ämneskategori)

Hitta via bibliotek

  • ACS Nano (Sök värdpublikationen i LIBRIS)

Till lärosätets databas

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy