Ether-free polyfluorenes tethered with quinuclidinium cations as hydroxide exchange membranes
-
- Allushi, Andrit (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
- Pham, Thanh Huong (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
- Olsson, Joel (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
visa fler...
-
- Jannasch, Patric (författare)
- Lund University,Lunds universitet,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
visa färre...
-
(creator_code:org_t)
- 2019
- 2019
- Engelska 11 s.
-
Ingår i: Journal of Materials Chemistry A. - 2050-7488. ; 7:47, s. 27164-27174
- Relaterad länk:
-
http://dx.doi.org/10... (free)
-
visa fler...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- We report on aryl ether-free 2,7-diphenylfluorene-based copolymers tethered with quinuclidinium (Qui) cations via hexyl spacers, prepared through superacid catalyzed Friedel Crafts polycondensation and quaternization reactions. The 2,7-diphenylfluorene monomers were prepared by Suzuki coupling and employed to increase polymer backbone stiffness. Corresponding copolymers and anion-exchange membranes (AEMs) tethered with piperidinium (Pip) and trimethylalkyl ammonium (TMA) cations were prepared as reference materials. At a given water content, the AEM functionalized with Qui cations was the most efficient hydroxide conductor and reached 100 mS cm-1 at 80 °C at an ion exchange capacity of 2.0 mequiv g-1. Moreover, this membrane showed the highest thermal and alkaline stability in the series. 1H NMR analysis of AEMs stored in 2 M aq. NaOH at 90 °C over 672 h revealed the complete absence of ring-opening β-elimination in the bicyclic cage-like Qui structure, and only ~1% β-elimination in the hexyl spacer. In contrast, the Pip cations were found to degrade via β-elimination in both the monocyclic ring structure and the hexyl spacer. Results on the Pip-modified AEM implied that a β-hydrogen in the linear alkyl spacer chain was approximately 4 times more vulnerable to elimination than a β-hydrogen in the 6-membered ring. In addition, all the cations degraded via substitution reactions to some degree, and the total loss of Qui, Pip and TMA cations over the period was estimated to 4, 12 and 9%, respectively. The overall findings demonstrate that the combination of aryl-ether free backbone polymers and Qui cations results in durable and high-performance AEMs suitable for use in alkaline electrochemical energy conversion and storage devices.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik -- Polymerteknologi (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering -- Polymer Technologies (hsv//eng)
- NATURVETENSKAP -- Kemi -- Materialkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Materials Chemistry (hsv//eng)
- NATURVETENSKAP -- Kemi -- Polymerkemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences -- Polymer Chemistry (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas