Visualizing the Mechanism Switching in High-Temperature Au-Catalyzed InAs Nanowire Growth
-
- Escobar Steinvall, Simon (författare)
- Lund University,Lunds universitet,NanoLund: Centre for Nanoscience,Annan verksamhet, LTH,Lunds Tekniska Högskola,Centrum för analys och syntes,Kemiska institutionen,Institutioner vid LTH,Other operations, LTH,Faculty of Engineering, LTH,Centre for Analysis and Synthesis,Department of Chemistry,Departments at LTH,Faculty of Engineering, LTH
-
- Johansson, Jonas (författare)
- Lund University,Lunds universitet,NanoLund: Centre for Nanoscience,Annan verksamhet, LTH,Lunds Tekniska Högskola,Other operations, LTH,Faculty of Engineering, LTH
-
- Lehmann, Sebastian (författare)
- Lund University,Lunds universitet,NanoLund: Centre for Nanoscience,Annan verksamhet, LTH,Lunds Tekniska Högskola,Other operations, LTH,Faculty of Engineering, LTH
- visa fler...
- visa färre...
- (creator_code:org_t)
- 2023
- 2023
- Engelska 5 s.
- Ingår i: Crystal Growth and Design. - 1528-7483. ; 23:9, s. 6228-6232
- Tidskriftsartikel (refereegranskat)
Abstract
Ämnesord
Stäng
- We use environmental transmission electron microscopy to observe in situ the switch from an axial vapor-liquid-solid (VLS) growth mechanism in Au-catalyzed InAs nanowires toward a radial vapor-solid (VS) one, dominated by layers nucleating at the triple-phase line. At elevated temperatures, in addition to high V/III ratios, the affinity for In in the Au catalyst will be greater than that of In in InAs, which in turn reduces the driving force and probability for nucleation at the liquid-solid interface. Consequently, with increased temperature, the catalyst particle stops acting as a sink for incoming material and the decomposition of precursors away from the catalyst increases, making radial vapor-solid growth the dominating growth mechanism. It is further observed that the growth proceeds through multistep propagation rather than a layer-by-layer propagation under these conditions.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
- Crystal Growth and Design (Sök värdpublikationen i LIBRIS)
Till lärosätets databas
- 1 av 1
- Föregående post
- Nästa post
- Till träfflistan
Hitta mer i SwePub
- Av författaren/redakt...
- Escobar Steinval ...
- Johansson, Jonas
- Lehmann, Sebasti ...
- Tornberg, Marcus
- Jacobsson, Danie ...
- Dick, Kimberly A ...
- Om ämnet
-
- TEKNIK OCH TEKNOLOGIER
- TEKNIK OCH TEKNO ...
- och Materialteknik
- och Metallurgi och m ...
- Artiklar i publikationen
- Crystal Growth a ...
- Av lärosätet
- Lunds universitet
Sök utanför SwePub
- Sök vidare i:
- Google Book Search
- Google Scholar
Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.
- Copyright © LIBRIS - Nationella bibliotekssystem
- LIBRIS.kb.se