Diameter-Dependent Photocurrent in InAsSb Nanowire Infrared Photodetectors.
-
- Svensson, Johannes (author)
- Lund University,Lunds universitet,Institutionen för elektro- och informationsteknik,Institutioner vid LTH,Lunds Tekniska Högskola,Department of Electrical and Information Technology,Departments at LTH,Faculty of Engineering, LTH
-
- Anttu, Nicklas (author)
- Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
-
- Vainorius, Neimantas (author)
- Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
-
show more...
-
- Borg, Mattias (author)
- Lund University,Lunds universitet,Fasta tillståndets fysik,Fysiska institutionen,Institutioner vid LTH,Lunds Tekniska Högskola,Solid State Physics,Department of Physics,Departments at LTH,Faculty of Engineering, LTH
-
- Wernersson, Lars-Erik (author)
- Lund University,Lunds universitet,Institutionen för elektro- och informationsteknik,Institutioner vid LTH,Lunds Tekniska Högskola,Fasta tillståndets fysik,Fysiska institutionen,Department of Electrical and Information Technology,Departments at LTH,Faculty of Engineering, LTH,Solid State Physics,Department of Physics,Faculty of Engineering, LTH
-
show less...
-
(creator_code:org_t)
- 2013-03-08
- 2013
- English.
-
In: Nano Letters. - : American Chemical Society (ACS). - 1530-6992 .- 1530-6984. ; 13:4, s. 1380-1385
- Related links:
-
https://portal.resea... (primary) (free)
-
show more...
-
http://dx.doi.org/10...
-
https://lup.lub.lu.s...
-
https://lup.lub.lu.s...
-
https://doi.org/10.1...
-
show less...
Abstract
Subject headings
Close
- Photoconductors using vertical arrays of InAs/InAs1-xSbx nanowires with varying Sb composition x have been fabricated and characterized. The spectrally resolved photocurrents are strongly diameter dependent with peaks, which are red-shifted with diameter, appearing for thicker wires. Results from numerical simulations are in good agreement with the experimental data and reveal that the peaks are due to resonant modes that enhance the coupling of light into the wires. Through proper selection of wire diameter, the absorptance can be increased by more than 1 order of magnitude at a specific wavelength compared to a thin planar film with the same amount of material. A maximum 20% cutoff wavelength of 5.7 μm is obtained at 5 K for a wire diameter of 717 nm at a Sb content of x = 0.62, but simulations predict that detection at longer wavelengths can be achieved by increasing the diameter. Furthermore, photodetection in InAsSb nanowire arrays integrated on Si substrates is also demonstrated.
Subject headings
- TEKNIK OCH TEKNOLOGIER -- Nanoteknik -- Nanoteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Nano-technology -- Nano-technology (hsv//eng)
Publication and Content Type
- art (subject category)
- ref (subject category)
Find in a library
To the university's database