Secondary corrosion protection of FeCr(Al) model alloys at 600 °C – The influence of Cr and Al after breakaway corrosion

• The influence of Cr and Al content on the oxidation behaviour of FeCr(Al) model alloys after breakaway oxidation at 600 °C and the underlying mechanisms were investigated in detail with thermogravimetrical analysis (TGA), thermodynamic calculations and advanced electron microscopy. The results showed that a Cr-content of ≥18 wt% drastically reduced the growth rate of the Fe-rich oxide scale, formed after breakaway oxidation, for FeCrAl alloys but not for FeCr alloys. This was attributed to the ability of the Fe(18-25)CrAl alloys to prevent internal oxidation, which enables the formation of a healing layer.

Ämnesord

NATURVETENSKAP  -- Kemi -- Annan kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Other Chemistry Topics (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Korrosionsteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Corrosion Engineering (hsv//eng)

Nyckelord

A. Chromium

A. Aluminium

A. FeCrAl

C. Internal oxidation

B. STEM

C. High temperature corrosion

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)