Sökning: id:"swepub:oai:research.chalmers.se:50971f30-0d45-4b5c-99a0-d6d6bcae48c5" >
Precipitation Kinet...
Precipitation Kinetics and Morphology of Grain Boundary Carbides in Ni-Base Superalloy Haynes 282
-
- Joseph, Ceena, 1982 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Persson, Christer, 1960 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Hörnqvist Colliander, Magnus, 1979 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
(creator_code:org_t)
- 2020-10-06
- 2020
- Engelska.
-
Ingår i: Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science. - : Springer Science and Business Media LLC. - 1073-5623. ; 51:12, s. 6136-6141
- Relaterad länk:
-
https://research.cha... (primary) (free)
-
visa fler...
-
https://link.springe...
-
https://research.cha...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Precipitation of grain boundary carbides in a mill-annealed Haynes 282 in the temperature range 650 degrees C to 1120 degrees C was investigated. The kinetics of M(23)C(6)was significantly faster than that of M6C. With increasing aging temperature, the morphology changes from continuous film to an interconnected brick wall structure and finally to discrete particles. No morphological changes were observed with aging time. Serrated grain boundaries formed during aging around 750 degrees C. The solvus temperature for both M(23)C(6)and M6C was approximately 1100 degrees C.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Teknisk mekanik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Applied Mechanics (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas