A Microstructural and Kinetic Investigation of the KCl-Induced Corrosion of an FeCrAl Alloy at 600 A degrees C
-
- Israelsson, Niklas, 1983 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Unocic, K.A. (författare)
- Oak Ridge National Laboratory
-
- Hellström, Kristina M, 1971 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Jonsson, Torbjörn, 1970 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Norell, Mats, 1961 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Svensson, Jan-Erik, 1965 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Johansson, Lars-Gunnar, 1952 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2015-03-18
- 2015
- Engelska.
-
Ingår i: Oxidation of Metals. - : Springer Science and Business Media LLC. - 1573-4889 .- 0030-770X. ; 84:1-2, s. 105-127
- Relaterad länk:
-
https://research.cha... (primary) (free)
-
visa fler...
-
https://link.springe...
-
https://research.cha...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- The corrosion behaviour of a FeCrAl alloy was investigated at 600 A degrees C in O-2 + H2O with solid KCl applied. A kinetics and microstructural investigation showed that KCl accelerates corrosion and that potassium chromate formation depletes the protective scale in Cr, thus triggering the formation of a fast-growing iron-rich scale. Iron oxide was found to grow both inward and outward, on either side of the initial oxide. A chromia layer is formed with time underneath the iron oxide. It was found that although the alloy does not form a continuous pure alumina scale at the investigated temperature, aluminium is, however, always enriched at the oxide/alloy interface.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- High-temperature corrosion
- KCl
- FeCrAl
- Water vapour