Comparison of early stages of precipitation in Mo-rich and Mo-poor maraging stainless steels
-
- ANDERSSON, MARCUS, 1976 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Stiller, Krystyna Marta, 1947 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Hattestrand, M. (författare)
- Sandvik Group AB
-
(creator_code:org_t)
- 2007
- 2007
- Engelska.
-
Ingår i: Surface and Interface Analysis. - : Wiley. - 1096-9918 .- 0142-2421. ; 39:2-3, s. 195-200
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://doi.org/10.1...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- The precipitation process during ageing in the Mo-poor alloy Carpenter 455 has been investigated by three-dimensional atom probe (3DAP) and energy-filtered transmission electron microscopy. The ageing treatment was performed at 475 degrees C for 5 min, 25 min, 1 h and 2 h. The precipitation of a mixed Ni-, Ti- and Cu-rich phase was observed after 25 min of ageing. A complete separation between Ni/Ti-rich and Cu-rich regions occurred within 1-2 h of ageing. After 2 h of ageing at 475 degrees C, coarsening of the eta-Ni3Ti precipitates was observed. Moreover, large Ni/Ti-rich and Cu-rich particles were observed in the lath boundaries after 2 h of ageing. The results were compared with the precipitation process in the Mo-rich alloy 1RK91. Copyright (C) 2007 John Wiley & Sons, Ltd.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Annan teknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Other Engineering and Technologies (hsv//eng)
Nyckelord
- atom probe
- maraging steels
- precipitation
- ageing