High temperature deformation of polycrystalline C40 Mo(Si,Al) 2
-
- Edgren, Aina, 1995 (författare)
- Kanthal AB,Chalmers tekniska högskola,Chalmers University of Technology
-
- Strom, E. (författare)
- Kanthal AB
-
- Qiu, Ren, 1993 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Frisk, Lars (författare)
- Luleå tekniska universitet (LTU),Luleå University of Technology (LTU)
-
- Akhtar, Farid (författare)
- Luleå tekniska universitet (LTU),Luleå University of Technology (LTU)
-
- Hörnqvist Colliander, Magnus, 1979 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2022
- 2022
- Engelska.
-
Ingår i: Materials Science & Engineering A: Structural Materials: Properties, Microstructure and Processing. - : Elsevier BV. - 0921-5093. ; 849
- Relaterad länk:
-
https://research.cha... (primary) (free)
-
visa fler...
-
https://research.cha...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Polycrystalline Mo(Si,Al)2 with C40 crystal structure was deformed in compression with a strain rate of 10−4 s−1 at 1300 °C. The specimens were deformed to a strain of 10%–15% and showed maximum stresses around 150 MPa prior to pronounced softening. No crack formation or significant increase in porosity could be observed. Post-test microstructure analysis revealed that the material was inhomogeneously deformed on both inter- and intragranular levels. Dynamic recrystallization occurred alongside low angle grain boundary formation in highly deformed grains. Furthermore, complex intragranular deformation fields suggest that slip systems other than 21̄1̄0[0001] may be active during deformation.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Maskinteknik -- Teknisk mekanik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Mechanical Engineering -- Applied Mechanics (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)
Nyckelord
- Dynamic recrystallization
- Ceramics
- High temperature compression
- Electron backscatter diffraction
- Mo(Si,Al) 2
- Low angle grain boundaries
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas