Microstructure of a Creep-Resistant 10 Pct Chromium Steel Containing 250 ppm Boron
-
- Golpayegani, Ardeshir, 1975 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Liu, Fang, 1975 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Svensson, Henrik, 1982 (författare)
- RISE,SWECAST
-
visa fler...
-
- ANDERSSON, MARCUS, 1976 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Andrén, Hans-Olof, 1947 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2010-12-02
- 2011
- Engelska.
-
Ingår i: Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science. - : Springer Science and Business Media LLC. - 1073-5623 .- 1543-1940. ; 42:4, s. 940-951
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
http://rd.springer.c...
-
https://doi.org/10.1...
-
https://research.cha...
-
https://urn.kb.se/re...
-
visa färre...
Abstract
Ämnesord
Stäng
- The microstructure of a trial martensitic chromium steel containing a high content of boron (250 ppm) was characterized in detail in the as-tempered and aged conditions. This steel has a similar composition and heat treatment as the TAF steel that still is unsurpassed in creep strength among all 9 to 12 pct chromium steels. Characterization was performed by using scanning electron microscopy, energy-filtered transmission electron microscopy, secondary ion mass spectroscopy, and atom probe tomography. Focus was placed on investigating different types of precipitates that play a key role in improving the creep resistance of these steels. The low tempering temperature of 963 K (690 A degrees C) is enough for the precipitation of the full volume fraction of both MX and M23C6. A high boron content, more than 1 at. pct, was found in M23C6 precipitates and they grow slowly during aging. The high boron level in the steel results in metal borides rather than BN with the approximate formula (Mo0.66Cr0.34)(2)(Fe0.75V0.25)B-2. Two families of MX precipitates were found, one at lath boundaries about 35 nm in size and one dense inside the laths, only 5 to 15 nm in size.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas