Determination of Stresses and Retained Austenite in Carbon Steels by X-rays - A Round Robin Study

• Residual stresses and retained austenite are twoimportant process-related parameters which need to becontrolled and monitored carefully during production andheat treatment of products. X-ray diffraction techniques arenormally used in this context, and the purpose of thepresent study was to investigate the reproducibility andaccuracy of these methods for medium and high carbonsteels. The work was carried out as a round robin studyincluding nine different laboratories in Sweden and Finland.Stress measurements were carried out on three specimens etched to three different depths, 0 μm, 230 μm and 515 μm. Retained austenite measurements were carried out on three specimens containing approximately 11, 17 and 30 vol.-% of this phase. The stress measurements showed good reproducibility with standard deviations of typically 4% on flat and smooth surfaces and not more than about 8% on etched surfaces. Estimations revealed that specimen misalignment and improper X-ray spot location were the main sources behind the variation in the stress recordings. The determination of retained austenite showed a standard deviation of typically 15% between the different contributors. However, by using identical evaluation methodsfor all raw data, the data spread could be narrowed by afactor of 3 to 4 despite the fact that different experimental settings were used in the individual laboratories.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Metallurgi och metalliska material (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Metallurgy and Metallic Materials (hsv//eng)

Nyckelord

Reproducibility

Residual stress

Round robin study

Accuracy

X-ray diffraction

Retained austenite

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)