Characterisation of structure and conductivity of BaTi0.5Sc 0.5O3 - δ
-
- Rahman, Seikh Mohammad Habibur, 1976 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Ahmed, Istaq, 1972 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Haugsrud, R. (författare)
- Universitetet i Oslo,University of Oslo
-
visa fler...
-
- Eriksson, Sten, 1958 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Knee, Christopher, 1973 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- Elsevier BV, 2014
- 2014
- Engelska.
-
Ingår i: Solid State Ionics. - : Elsevier BV. - 0167-2738. ; 255, s. 140-146
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://doi.org/10.1...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- BaTi0.5Sc0.5O3 - δ was prepared via solid state reaction route and final sintering at 1550 C. High resolution X-ray powder diffraction on the as-prepared material reveals a cubic perovskite structure with a unit cell parameter, a = 4.1343(1) Å. Thermogravimetric analysis revealed the presence of significant levels of protons in the as-prepared material and 74% of the theoretically achievable protonation through filling of oxide ion vacancies was attained on exposure to a humid environment at 185 C. Infrared spectroscopy revealed a broad OH stretching band confirming the presence of OHO • defects. Electrical conductivity was measured with variable frequency AC impedance methods in oxygen, argon, and hydrogen under dry, hydrated (H2O) and heavy water (D2O) conditions. In the temperature range of 150-550 C in a wet gas atmosphere the conductivity is significantly higher than that observed for dry conditions, indicating that protons are the dominant charge carriers. Conductivity is also found to be higher in dry oxygen in comparison with dry argon over the whole temperature range of 150-1000 C, characteristic of contribution from p-type charge carriers under oxidising atmospheres. At 550 C the proton conductivity was estimated to be 2.89 × 10- 4 S cm- 1 in wet Ar. Fitting of conductivity data provides a hydration enthalpy change (ΔH hydr 0) of - 100 ± 5 kJ/mol and hydration entropy change (ΔShydr 0) of - 160 ± 10 J/mol K.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
- NATURVETENSKAP -- Fysik (hsv//swe)
- NATURAL SCIENCES -- Physical Sciences (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Kemiteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Chemical Engineering (hsv//eng)
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Nyckelord
- BaTiO3
- Perovskite
- Hydration
- Proton conductivity
- X-ray diffraction
- Barium titanate