Initial stages of the HCl-induced high-temperature corrosion of alloy 310
-
- Folkeson, Nicklas, 1981 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Johansson, Lars-Gunnar, 1952 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Svensson, Jan-Erik, 1965 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
(creator_code:org_t)
- 2007
- 2007
- Engelska.
-
Ingår i: Journal of the Electrochemical Society. - 1945-7111 .- 0013-4651. ; , s. 515-521
- Relaterad länk:
-
https://research.cha...
Abstract
Ämnesord
Stäng
- Polished 310 stainless steel coupons were exposed isothermally in a horizontal tube furnace at 500 C for 1-168 h. The exposure gas consisted of N-2 with 5% O-2 and 500 ppm HCl(g). The corroded samples were analyzed by X-ray diffraction, focused ion beam microanalysis, scanning electron microscopy with energy-dispersive X-ray analysis, and by Auger electron spectroscopy. Mass gain was recorded. As expected, HCl (g) is a corrosion accelerator, the dominating corrosion products being FeCl2, Fe2O3, and Cr2O3. A tentative mechanism for the initial stages of the HCl-induced corrosion of stainless steel is presented. (c) 2007 The Electrochemical Society.
Ämnesord
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Publikations- och innehållstyp
- art (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas