Dynamic strain aging in Haynes 282 superalloy
-
- Hörnqvist Colliander, Magnus, 1979 (författare)
- GKN Aerospace Sweden AB,Chalmers tekniska högskola,Chalmers University of Technology
-
- Joseph, Ceena, 1982 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Persson, Christer, 1960 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Weidow, Jonathan, 1980 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Lai, Haiping, 1979 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa färre...
-
(creator_code:org_t)
- 2014-08-29
- 2014
- Engelska.
-
Ingår i: MATEC Web of Conferences. - : EDP Sciences. - 2261-236X. ; 14, s. Art. no. 16002-
- Relaterad länk:
-
http://publications.... (primary) (free)
-
visa fler...
-
https://www.matec-co...
-
https://research.cha...
-
https://doi.org/10.1...
-
visa färre...
Abstract
Ämnesord
Stäng
- Haynes 282 is a newly introduced Ni-based superalloy, developed to provide a combination of high-temperature mechanical properties, thermal stability and processability. The present contribution investigates the effect of dynamic strain aging (DSA) on the deformation behaviour of Haynes 282 during monotonic and cyclic loading. It is shown that DSA (presumably related to carbon diffusion based on rough estimates of the activation energy) completely dominates the development of the stress during cycling at intermediate temperatures, leading to extensive cyclic hardening and serrated yielding. However, no clear effects on the fatigue life or the resulting dislocation structure could be observed. The tensile properties were not severely affected, in spite of the presence of extensive serrated yielding, although a reduction in ductility was observed in the DSA temperature regime. During monotonic loading at lower strain rates indications of an additional DSA mechanism due to substitutional elements were observed.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering (hsv//eng)
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
Publikations- och innehållstyp
- kon (ämneskategori)
- ref (ämneskategori)
Hitta via bibliotek
Till lärosätets databas