A comparison of NOx adsorption on Na, H and BaZSM-5 films

• NOx adsorption in ZSM-5 films containing Na+, H+ or Ba2+ as counter ions was studied. NaZSM-5 films showed a superior NOx adsorption capacity over the entire temperature range (30-350ºC) in comparison with the other films. Besides the possibility to form strongly bound surface nitrate species, the presence of the Na ions in ZSM-5 resulted in a large enhancement of various weakly adsorbed species. In the HZSM-5 film, the NOx adsorption was mainly due to physisorption, surface nitric acid and nitrosium ion (NO+) formation. Besides weakly adsorbed species and surface nitric acid, the NOx adsorption in BaZSM-5 films also resulted in formation of strongly bound surface nitrate species. The nitrate species in the BaZSM-5 film were found to be resistant to NO exposure and were mainly formed through an NO2 disproportionation pathway.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Kemiteknik -- Kemiska processer (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Chemical Engineering -- Chemical Process Engineering (hsv//eng)

Nyckelord

counter ions

NOx adsorption

monolith

ZSM-5 films

Chemical Technology

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)