Abrasive wear comparison of Cr3C2/Ni3Al composite and stellite 12 alloy cladding

• The room-temperature abrasive wear resistance of Cr3C2/Ni3Al composite and Stellite12 alloy cladding was investigated. Three kinds of tests, designed for different load and abrasive' size, were utilized to understand the wear behaviour of these materials. Under all three wear conditions, the abrasion resistance of Cr3C2/Ni3Al composite cladding is much higher than Stellite 12 alloy. In addition, the wear-resistant advantage of Cr3C2/Ni3Al composite is more obvious when the size of the abrasive is small. The relative wear resistance of Cr3C2/Ni3Al composite increases from 2.44 times to 6 times when the size of the abrasive decreases from 180 mu m to 50 mu m. The good wear resistance of Cr3C2/Ni3Al composite cladding can be mainly attributed to the high hardness, large volume fraction of reinforcement, large reinforcement particles, and size distribution of reinforcement.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

Nyckelord

METAL-MATRIX COMPOSITES

stellite12

NICKEL

composity

PERFORMANCE

MICROSTRUCTURE

abrasive wear

chromium carbide

TEMPERATURE

Ni3Al

Publikations- och innehållstyp

art (ämneskategori)

ref (ämneskategori)