The effect of the polymerisation temperature on molecular weight and photoluminescence quantum yield for a phenylsubstituted PPV

Andersson, M.R.Department of Polymer Technology, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden (författare)

We present the synthesis and characterisation of poly(2-(2',5'-bis(2?-ethylhexyloxy)phenyl)-1, 4-phenylenevinylene) (BEHP-PPV) polymerised under different conditions. The photoluminescence efficiencies (?PL) in the solid state of BEHP-PPV obtained at 144°C and 0°C are 28% and 60%, respectively. Polymerisation temperatures below 0°C decreases the molecular weight without changing the photoluminescence efficiency to any large extent.

Johansson, D.M.Department of Organic Chemistry, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden (författare)
Theander, M. (författare)
Inganäs, OlleLinköpings universitet,Tekniska högskolan,Biomolekylär och Organisk Elektronik(Swepub:liu)ollin59 (författare)
Department of Polymer Technology, Chalmers University of Technology, SE-412 96 Gothenburg, SwedenDepartment of Organic Chemistry, Chalmers University of Technology, SE-412 96 Gothenburg, Sweden (creator_code:org_t)

Av författaren/redakt...: Andersson, M.R.; Johansson, D.M.; Theander, M.; Inganäs, Olle

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.