Field-effect transistors with thin ZnO as active layer for gas sensor applications

Tyck till om SwePub Sök här!

Zinc oxide based field-effect devices prepared for gas sensing applications are studied. For this purpose, bottom-gate transistors were fabricated using Pd as source and drain interdigitated electrodes with gate lengths varying from 0.3 to 2 mu m. Thin (50 nm) zinc oxide films were grown with the aid of pulsed laser deposition (PLD) at room temperature and served as active and sensing layer. AFM and XRD analysis demonstrated the polycrystalline nature of the c-axis oriented ZnO films with nanoscale grain size (20-40 nm) with relatively high average roughness. Electrical and gas sensing measurements from the above-mentioned devices are presented. (C) 2008 Elsevier B.V. All rights reserved.

Speliotis, T. (författare)
Alexandrou, K. P. (författare)
Tsamis, C. (författare)
Kompitsas, M. (författare)
Fasaki, I. (författare)
Jedrasik, Piotr,1957Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)pije (författare)
Petersson, Göran,1946Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)gope (författare)
Nilsson, Bengt,1954Chalmers tekniska högskola,Chalmers University of Technology(Swepub:cth)beni (författare)
Chalmers tekniska högskola (creator_code:org_t)

Av författaren/redakt...: Farmakis, F. V.; Speliotis, T.; Alexandrou, K. P ...; Tsamis, C.; Kompitsas, M.; Fasaki, I.; visa fler...; Jedrasik, Piotr, ...; Petersson, Göran ...; Nilsson, Bengt, ...; visa färre...

Om ämnet

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.