Effect of co-doping on proton conductivity in perovskite oxides BaZr0.9In0.05M0.05O3−δ (M = Yb3+ or Ga3+)

• BaZr0.9In0.05M0.05O3-d (M ¼ Ga3+ or Yb3+) has been prepared by solid-statesynthesis route.Rietveld analysis of neutron powder diffraction data on as-prepared samples showed thatboth samples crystallise in the cubic space group Pm-3m. Scanning electron microscopyanalysis showed that the grains intheBaZr0.9In0.05Ga0.05O3-d sample were larger than the BaZr0.9In0.05Yb0.05O3-d sample. Dynamic thermogravimetric analysis indicates that the proton concentration was higher inpre-hydrated BaZr0.9In0.05Ga0.05O3-d sample (40%oftheoretical)than that of BaZr0.9In0.05Yb0.05O3-d sample (28%oftheoretical).Proton conductivity was studied on pre-hydrated samples(under both dry and wetAr atmospheres).Thebulk proton conductivities of the heating cycle of pre-hydrated BaZr0.9In0.05M0.05O3-d (M ¼ Ga3+ or Yb3+) samples were 2.1 * 10-5 S cm-1 and 1.9 * 10-4 Scm-1 at 350C, respectively.The effect of co-doping onproton conductivity was investigatedand the results are compared with single doped systems e.g. BaZr0.9M0.1O3-d (M=Ga3+, In3+ orYb3+) samples.

Subject headings

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)

TEKNIK OCH TEKNOLOGIER  -- Materialteknik -- Annan materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering -- Other Materials Engineering (hsv//eng)

Keyword

TGA

Proton conductor

Rietveld analysis

SEM

Neutron diffraction

Impedance spectroscopy

Neutron diffraction; Rietveld analysis; TGA; SEM; Proton conductor; Impedance spectroscopy

Publication and Content Type

art (subject category)

ref (subject category)