Improved Proton Conductivity in Spark-Plasma Sintered Dense Ceramic BaZr0.5In0.5O3-delta

• Spark-plasma sintering method was used to prepare dense proton conducting perovskite oxide BaZr0.5In0.5O3-delta. Analysis of X-ray powder diffraction data showed that the sample adopt the cubic crystal structure having the space group Pm3m. Thermogravimetric analysis of prehydrated samples showed significant mass losses beyond 300 degrees C due to loss of protons as water vapor. Scanning electron microscope images show that the grain size of the spark-plasma sintered dense sample was smaller than that of solid-state sintered porous sample. The highest total proton conductivity (2 X 10(-3) S cm(-1) at 450 degrees C) was found for dense spark-plasma sintered sample under wet H-2 than the samples prepared by other routes.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)

NATURVETENSKAP  -- Kemi (hsv//swe)

NATURAL SCIENCES  -- Chemical Sciences (hsv//eng)

Nyckelord

transport-properties

chemical-stability

doped bazro3

oxides

bazr0.9y0.1o2.95

conductors

hydrogen

baceo3

conductors

NATURAL SCIENCES

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)