Proton Conductivity in Mixed B-Site Doped Perovskite Oxide BaZr[sub 0.5]In[sub 0.25]Yb[sub 0.25]O[sub 3 - delta]
-
- Ahmed, Istaq, 1972 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
Kinyanjui, Francis G., 1981 (författare)
-
- Rahman, Seikh Mohammad Habibur, 1976 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
visa fler...
-
- Steegstra, Patrick, 1978 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kemi,Department of Chemistry,University of Gothenburg
-
- Eriksson, Sten, 1958 (författare)
- Chalmers tekniska högskola,Chalmers University of Technology
-
- Ahlberg, Elisabet, 1952 (författare)
- Gothenburg University,Göteborgs universitet,Institutionen för kemi,Department of Chemistry,University of Gothenburg
-
visa färre...
-
(creator_code:org_t)
- The Electrochemical Society, 2010
- 2010
- Engelska.
-
Ingår i: Journal of The Electrochemical Society. - : The Electrochemical Society. - 0013-4651 .- 1945-7111. ; 157:12, s. B1819-B1824
- Relaterad länk:
-
http://dx.doi.org/10...
-
visa fler...
-
https://gup.ub.gu.se...
-
https://doi.org/10.1...
-
https://research.cha...
-
visa färre...
Abstract
Ämnesord
Stäng
- A wet chemical route was used to prepare the oxygen deficient codoped perovskite oxide BaZr0.5In0.25Yb0.25O3−. Analysis of X-ray powder diffraction data showed that the sample belongs to the cubic crystal system with space group Pmm. Dynamic thermogravimetric (TG) analysis confirmed complete filling of oxygen vacancies (V) by protonic defects (OH) during the hydration process. The proton conductivity was investigated by impedance spectroscopy. The bulk and total conductivities of prehydrated BaZr0.5In0.25Yb0.25O3− were found to be 8.5×10−4 and 2.2×10−5 S cm−1, respectively, at 300°C. The total conductivity in the codoped perovskite oxide was higher compared to that of the respective single doped perovskite oxides with the same doping level. The bulk and grain-boundary mobility and diffusion coefficients of protons were calculated at 200°C using impedance and TG data to obtain the conductivity and proton concentration, respectively. The high bulk diffusivity (2.3×10−7 cm2 s−1) was obtained which indicates that the protons are more free to move in the heavily doped matrix compared to the lightly doped systems where trapping of protons occurs.
Ämnesord
- TEKNIK OCH TEKNOLOGIER -- Materialteknik -- Annan materialteknik (hsv//swe)
- ENGINEERING AND TECHNOLOGY -- Materials Engineering -- Other Materials Engineering (hsv//eng)
- NATURVETENSKAP -- Kemi (hsv//swe)
- NATURAL SCIENCES -- Chemical Sciences (hsv//eng)
Nyckelord
- barium compounds
- proton exchange membrane fuel cells
- thermal analysis
- vacancies (crystal)
- X-ray diffraction
- zirconium compounds
- barium compounds
Publikations- och innehållstyp
- ref (ämneskategori)
- art (ämneskategori)
Hitta via bibliotek
Till lärosätets databas