Mesoporous Titania for High Rate Electrochemical Energy Storage

Calcagno, Giulio, 1990 (författare)
Chalmers tekniska högskola,Chalmers University of Technology
 (creator_code:org_t)
Gothenburg, 2019
Engelska.
  • Licentiatavhandling (övrigt vetenskapligt/konstnärligt)
Abstract Ämnesord
Stäng  
  • Mesoporous titanium oxides are increasingly attracting interest as potential candidates for fast electrochemical energy storage. In this thesis, mesoporous titania of different polymorphs have been evaluated in relation to their ability to reversibly store Li+ ions inside their structure. Mesoporous anatase beads with high crystallinity and specific morphology show high electrochemical capacity and high rate performance. The materials store charge through Li+ ion insertion of both faradaic and extrinsic pseudocapacitive nature. Moreover, the discharge capacity retention after 150 cycles is >95%. On the other hand, ordered mesoporous titania, prepared via low-temperature spray deposition and mainly amorphous, shows a linear correlation between voltage and capacity, typical of an intrinsic pseudocapacitive material of insertion type. The material exhibits exceptionally high electrochemical capacity of 680 mAh g-1 during the first cycle, which, however, rapidly decreases over the following cycles. A combination of electrochemical and structural characterization techniques is used to study the charge/discharge behavior of the material and the origin of the irreversible capacity. X-ray absorption spectroscopy and energy-filtered TEM are carried out to analyse pristine and cycled samples in charged and discharged state. The results suggest that the irreversible loss in the capacity is due to the formation of electrochemically inactive phases mainly located at the surface of the material. Additionally, electrodes based on mesoporous anatase beads are paired with a commercial activated carbon electrode that presents a broad distribution of mesopores and very high surface area to design a hybrid asymmetric supercapacitor. The device shows extraordinary stable performance with energy densities of 27 Wh kg-1 at the relatively fast discharge current of 2.5 A g-1 for 10 000 cycles and high power densities during fast cycling.

Ämnesord

NATURVETENSKAP  -- Kemi -- Oorganisk kemi (hsv//swe)
NATURAL SCIENCES  -- Chemical Sciences -- Inorganic Chemistry (hsv//eng)
TEKNIK OCH TEKNOLOGIER  -- Materialteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Materials Engineering (hsv//eng)
NATURVETENSKAP  -- Kemi -- Materialkemi (hsv//swe)
NATURAL SCIENCES  -- Chemical Sciences -- Materials Chemistry (hsv//eng)
TEKNIK OCH TEKNOLOGIER  -- Nanoteknik (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Nano-technology (hsv//eng)

Nyckelord

Mesoporous Titanium Dioxide
XAS
Pseudocapacitance
Hybrid Asymmetric Supercapacitors

Publikations- och innehållstyp

lic (ämneskategori)
vet (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Hitta mer i SwePub

Av författaren/redakt...
Calcagno, Giulio ...
Om ämnet
NATURVETENSKAP
NATURVETENSKAP
och Kemi
och Oorganisk kemi
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Materialteknik
NATURVETENSKAP
NATURVETENSKAP
och Kemi
och Materialkemi
TEKNIK OCH TEKNOLOGIER
TEKNIK OCH TEKNO ...
och Nanoteknik
Av lärosätet
Chalmers tekniska högskola

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy