Cobalt-chromium alloys fabricated with four different techniques: Ion release, toxicity of released elements and surface roughness

• Objective. To investigate the metal ion release, surface roughness and cytoxicity for Co-Cr alloys produced by different manufacturing techniques before and after heat treatment. In addition, to evaluate if the combination of materials affects the ion release. Methods. Five Co-Cr alloys were included, based on four manufacturing techniques. Commercially pure titanium, CpTi grade 4 and a titanium alloy were included for comparison. The ion release tests involved both Inductive Coupled Plasma Optical Emission Spectrometry and Inductive Coupled Plasma Mass Spectrometry analyses. The surface analysis was conducted with optical interferometry. Cells were indirectly exposed to the materials and cell viability was evaluated with the MTT (3-(4.5-dimethylthiazol-2-yl)-2.5-diphenyltetrazolium bromide) method. Results. All alloys showed a decrease of the total ion release when CpTi grade 4 was present. The total ion release decreased over time for all specimens and the highest ion release was observed from the cast and milled Co-Cr alloy in acidic conditions. The cast and laser-melted Co-Cr alloy and the titanium alloy became rougher after heat treatment. All materials were within the limits of cell viability according to standards. Significance. The ion release from Co-Cr alloys is influenced by the combination of materials, pH and time. Surface roughness is influenced by heat treatment. Furthermore, both ion release and surface roughness are influenced by the manufacturing technique and the alloy type. The clinical implication needs to be further investigated. (C) 2020 The Academy of Dental Materials. Published by Elsevier Inc.

Ämnesord

MEDICIN OCH HÄLSOVETENSKAP  -- Klinisk medicin -- Odontologi (hsv//swe)

MEDICAL AND HEALTH SCIENCES  -- Clinical Medicine -- Dentistry (hsv//eng)

Nyckelord

Prostho do ntics

Dental alloys

Manufacturing

Cobalt-chromium

Titanium

Corrosion

Metal ion release

Surface roughness

Cytotoxicity

corrosion-resistance

metal release

titanium

cytotoxicity

fibroblasts

responses

frameworks

retention

crowns

Dentistry

Oral Surgery & Medicine

Materials Science

Prostho do ntics

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)