Study of CuNiZnGdCe-Nanocomposite Anode for Low Temperature SOFC

• Composite electrodes of Cu0.16Ni0.27Zn0.37Ce0.16Gd0.04 (CNZGC) oxides have been successfully synthesized by solid state reaction method as anode material for low temperature solid oxide fuel cell (LTSOFC). These electrodes are characterized by XRD followed by sintering at various time periods and temperatures. Particle size of optimized composition was calculated 40-85 nm and sintered at 800 degrees C for 4 hours. Electrical conductivity of 4.14 S/cm was obtained at a temperature of 550 degrees C by the 4-prob DC method. The activation energy was calculated 4 x 10(-2) eV at 550 degrees C. Hydrogen was used as fuel and air as oxidant at anode and cathode sides respectively. I-V/I-P curves were obtained in the temperature range of 400-550 degrees C. The maximum power density was achieved for 570 mW/cm(2) at 550 degrees C.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Maskinteknik -- Energiteknik (hsv//swe)

ENGINEERING AND TECHNOLOGY  -- Mechanical Engineering -- Energy Engineering (hsv//eng)

Nyckelord

Nanocomposites

Electrodes

One Step Solid Oxide Fuel Cell

Low Temperature SOFC

Publikations- och innehållstyp

ref (ämneskategori)

art (ämneskategori)