Electropolished titanium implants with a mirror-like surface support osseointegration and bone remodelling

Larsson Wexell, Cecilia, 1965 (författare)
University of Gothenburg,Gothenburg University,Göteborgs universitet,Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap,Institute of Clinical Sciences, Department of Biomaterials
Shah, Furqan A. (författare)
University of Gothenburg,Gothenburg University,Göteborgs universitet,Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap,Institute of Clinical Sciences, Department of Biomaterials
Ericson, Lars (författare)
University of Gothenburg,Gothenburg University,Göteborgs universitet,Institutionen för biomedicin, avdelningen för medicinsk kemi och cellbiologi,Institute of Biomedicine, Department of Medical Biochemistry and Cell Biology
visa fler...
Matic, Alexandar (författare)
Palmquist, Anders, 1977 (författare)
University of Gothenburg,Gothenburg University,Göteborgs universitet,Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap,Institute of Clinical Sciences, Department of Biomaterials
Thomsen, Peter, 1953 (författare)
University of Gothenburg,Gothenburg University,Göteborgs universitet,Institutionen för kliniska vetenskaper, Avdelningen för biomaterialvetenskap,Institute of Clinical Sciences, Department of Biomaterials
Matic, Aleksandar, 1968 (författare)
Chalmers University of Technology,Chalmers tekniska högskola
visa färre...
 (creator_code:org_t)
 
visa fler...
 
 
 
visa färre...
2016
2016
Engelska.
Ingår i: Advances in Materials Science and Engineering. - 1687-8434 .- 1687-8442.
  • Tidskriftsartikel (refereegranskat)
Abstract Ämnesord
Stäng  
  • This work characterises the ultrastructural composition of the interfacial tissue adjacent to electropolished, commercially pure titanium implants with and without subsequent anodisation, and it investigates whether a smooth electropolished surface can support bone formation in a manner similar to surfaces with a considerably thicker surface oxide layer. Screw-shaped implants were electropolished to remove all topographical remnants of the machining process, resulting in a thin spontaneously formed surface oxide layer and a smooth surface. Half of the implants were subsequently anodically oxidised to develop a thickened surface oxide layer and increased surface roughness. Despite substantial differences in the surface physicochemical properties, the microarchitecture and the composition of the newly formed bone were similar for both implant surfaces after 12 weeks of healing in rabbit tibia. A close spatial relationship was observed between osteocyte canaliculi and both implant surfaces. On the ultrastructural level, the merely electropolished surface showed the various stages of bone formation, for example, matrix deposition and mineralisation, entrapment of osteoblasts within the mineralised matrix, and their morphological transformation into osteocytes. The results demonstrate that titanium implants with a mirror-like surface and a thin, spontaneously formed oxide layer are able to support bone formation and remodelling.

Ämnesord

TEKNIK OCH TEKNOLOGIER  -- Industriell bioteknik (hsv//swe)
MEDICIN OCH HÄLSOVETENSKAP  -- Klinisk medicin (hsv//swe)
MEDICIN OCH HÄLSOVETENSKAP  -- Medicinsk bioteknologi (hsv//swe)
ENGINEERING AND TECHNOLOGY  -- Industrial Biotechnology (hsv//eng)
MEDICAL AND HEALTH SCIENCES  -- Clinical Medicine (hsv//eng)
MEDICAL AND HEALTH SCIENCES  -- Medical Biotechnology (hsv//eng)

Nyckelord

Osseointegration; bone; titanium; electropolishing; anodic oxidation; in vivo

Publikations- och innehållstyp

ref (ämneskategori)
art (ämneskategori)

Hitta via bibliotek

Till lärosätets databas

Sök utanför SwePub

Kungliga biblioteket hanterar dina personuppgifter i enlighet med EU:s dataskyddsförordning (2018), GDPR. Läs mer om hur det funkar här.
Så här hanterar KB dina uppgifter vid användning av denna tjänst.

 
pil uppåt Stäng

Kopiera och spara länken för att återkomma till aktuell vy